This one-component 16 OZ pre-catalyzed cross-linking polyvinyl acetate adhesive offers fast cure and HPVA Type II water resistance. It has excellent spreading and layering characteristics with a high final cure strength that has a rigid glue line, ideal for veneering. This tough glue line is what sets it apart from other PVAs. Uses include laminating paper backed and raw wood veneer, porous material, bent laminations and general woodworking. It has a 68% solids content and is slightly tan in appearance. Occasionally the color will stratify in the bottle, but does not affect the bond or drying time. You can tip bottle upside down for 30 min to mix. It can be tinted with food dyes if need be, and larger surfaces can be wetted with multiple thin layers of glue applied with a foam roller, making the adhesive thickness controllable by sight. A warmer cure cycle will result in a stronger bond, and at 70° / 70% you should have a working time of 15 minutes before the project needs to be clamped. The spread rate is approx. 1 cup per 10 square feet. A heating blanket over the press will promote initial attack of adhesive. accelerate hardness and shorten cure time. At 100 degrees, the glue cures in 2 hours. At 75 degrees cure time is approximately 6 hours to unclamp. Note: Vacuum press clamp times may take longer since this adhesive cures by evaporation.